| Place of Origin: | China |
|---|---|
| Brand Name: | Acemien |
| Certification: | CE |
| Model Number: | SJZ80/156 |
| Minimum Order Quantity: | 1SET |
| Price: | NEGOTIATION |
| Packaging Details: | STANDARD PACKAGE OR FILM |
| Delivery Time: | 30 WORKING DAYS |
| Payment Terms: | L/C, T/T, Western Union |
| Supply Ability: | 150SETS/YEAR |
| Power(w): | 168KW | Product Type: | Foaming Machine, Foam Plate Making Machine |
|---|---|---|---|
| After-sales Service Provided: | Engineers Available To Service Machinery Overseas | Condition: | New |
| Warranty:: | 13 Months | Name: | Foam Thermocol Plate Making Machine PS Foam Plate Cups Box Machines, |
| Automatic: | Yes, Fully Automatic | Product Name: | Fully Automatic Polystyrene Foam Instant Food Container Making Machine |
| High Light: | wpc foam board production line,foam board production line |
||
Automatic Machine For Making Disposable Foam Plates Tray sponge mattress cutter
The production processing of PVC skin foam board is as follows:
PVC resin + additive → high speed mixing → low speed cold mixing → cone twin screw extrusion → die shaping (crust foaming) → cooling setting → multi-roller traction → cutting products → collection inspection
(1) It is suitable that the PVC resin powder has a polymerization degree of 700. Japan's S-1007, S-700, South Korea's LS-70, Shanghai chlor-alkali WS-700.
(2) Since calcium carbonate is easily damp, calcium carbonate is preferably a surface-treated light active calcium carbonate having a fineness of 800 mesh or more.
(3) The foaming accelerator composition contains a stabilizer and a foaming accelerator, and CN-010 is a heat-dissipating and blowing foaming agent, and it is necessary to use HYPET products.
(4) Adding about 30 pieces of crushed material is beneficial to the stability of the feed without affecting the foaming effect.
(5) AC foaming agent and CN-010 should pay special attention to moisture.
All other raw materials should be checked for moisture and precautions should be taken. After the materials are finished, the bags should be sealed in time to avoid moisture.
| None wood powder formula | With wood powder formula | ||
| CPE135AImpact modifier | 3 | CPE135AImpact modifier | 3 |
| Foaming regulatorZB-530 | 6 | Foaming regulatorZB-530 | 6 |
| AC Foaming reagent | 0.4 | AC Foaming reagent | 0.4 |
| Foaming accelerator composition | 5 | Foaming accelerator composition | 5 |
| CN-010 | 0.4 | CN-010 | 0.4 |
| NONE | Oxide wax PE | 0.1 | |
| PVC Resin powder | 75 | PVC Resin powder | 75 |
| Calcium carbonate | 23 | Calcium carbonate | 11.5 |
| NONE | Wood powder | 11.5 | |
| Epoxy soybean oil | 3 | Epoxy soybean oil | 4 |
| Foamed broken material | 10-30 | Foamed broken material | 10-30 |